Effect of different UV intensity on corrosion behavior of carbon steel exposed to simulated Nansha atmospheric environment

doi:10.1016/j.matchemphys.2019.121855

YIC-IR

	Effect of different UV intensity on corrosion behavior of carbon steel exposed to simulated Nansha atmospheric environment
	Liu, Yuwei 1,2; Zhang, Jian 3; Wei, Yinghua 1; Wang, Zhenyao 1
发表期刊	MATERIALS CHEMISTRY AND PHYSICS
ISSN	0254-0584
	2019-11-01
卷号	237 页码:7
关键词	Carbon steel UV intensity Nansha atmosphere Surface roughness
DOI	10.1016/j.matchemphys.2019.121855
通讯作者	Wang, Zhenyao([email protected])
英文摘要	Effect of UV intensity on the corrosion behavior of carbon steel exposed to simulated Nansha atmospheric environment has been investigated using weight loss measurement, a stereomicroscope, a laser scanning confocal microscope (LSCM), a scanning electron microscope (SEM), X-ray diffraction (XRD), and electrochemical impedance spectroscopy (EIS). According to the results, when UV intensity is higher enough, the corrosion rate was accelerated significantly. As UV intensity increasing, the surface roughness of the rusted sample was not changed much at the initial stage. After long time exposure, the roughness became lager and the rust layer became thicker with many voids and cracks distributing in the rust layer. The composition of corrosion products were the same, but the relative content of different kind FeOOH was changed as UV intensity increased.
资助机构	Chinese Academy of Sciences ; National Natural Science Foundation of China
收录类别	SCI
语种	英语
关键词[WOS]	ULTRAVIOLET-LIGHT IRRADIATION ; WEATHERING STEEL ; PHOTO-CORROSION ; NACL ; RUST ; ZINC ; MECHANISM ; PHOTOINHIBITION ; OZONE ; PART
研究领域[WOS]	Materials Science
WOS记录号	WOS:000489066200026
引用统计	被引频次：31[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.yic.ac.cn/handle/133337/34757
专题	中国科学院烟台海岸带研究所
通讯作者	Wang, Zhenyao
作者单位	1.Chinese Acad Sci, Environm Corros Ctr, Inst Met Res, Wencui Rd 62, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Wenhua Rd 72, Shenyang 110016, Liaoning, Peoples R China 3.Chinese Acad Sci, Anal & Testing Ctr, Inst Met Res, Wenhua Rd 72, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式 GB/T 7714	Liu, Yuwei,Zhang, Jian,Wei, Yinghua,et al. Effect of different UV intensity on corrosion behavior of carbon steel exposed to simulated Nansha atmospheric environment[J]. MATERIALS CHEMISTRY AND PHYSICS,2019,237:7.
APA	Liu, Yuwei,Zhang, Jian,Wei, Yinghua,&Wang, Zhenyao.(2019).Effect of different UV intensity on corrosion behavior of carbon steel exposed to simulated Nansha atmospheric environment.MATERIALS CHEMISTRY AND PHYSICS,237,7.
MLA	Liu, Yuwei,et al."Effect of different UV intensity on corrosion behavior of carbon steel exposed to simulated Nansha atmospheric environment".MATERIALS CHEMISTRY AND PHYSICS 237(2019):7.